Material 1.7220

Vergütungsstahl

Do you have any questions about the material or would you like to order? Complete our inquiry form, it`s free of charge and without obligation. We will get in touch with you in order to provide you with more information.

Standards

HDIN / EN	US-Standard	AFNOR	UNI	JIS	request
34CrMo4	AISI 4130 AISI 4135 AISI 4135H AISI 4137 AISI 4137H UNS G41300 UNS G41350 UNS G41370 UNS H41350 UNS H41370		34CrMo4KB 35CrMo4	SCM432 SCM435 SCM435H SCM435HRCH SCM435M SCM435RCH SCM435TK SCM435WCH	request

Material Category: Vergütungsstahl

Chemical Composition

C %	Si %	Mn %	P %	S %	Cr %	Mo %
0,30 - 0,37	max 0,40	0,60 - 0,90	max 0,035	max 0,035	0,90 - 1,20	0,15 - 0,30

Product Specifications

DIN EN 2446 (07/2009)
DIN EN 2448 (07/2009)
DIN EN 3329 (08/2009)
DIN EN 3330 (06/2009)
DIN EN 10083-3 (01/2007)
DIN EN 10132-3 (05/2000)
DIN EN 10250-3 (12/1999)
DIN EN 10263-4 (02/2018)
DIN EN 10277 (09/2018)
DIN EN 10297-1 (06/2003)
DIN EN ISO 683-2 (09/2018)
DIN SEW 310 (08/1992)
DIN SEW 550 (08/1976)
- WL

Mechanical Properties

DIN EN 10083-3 (01/2007) Vergütungsstähle. Legierte Stähle.
weichgeglüht	Härte [HBW]	<= 223 HBW

abgeschreckt	Stirnabschreckversuch nach Jominy (+H)	Stirnabschreckversuch nach Jominy (+HH)	Stirnabschreckversuch nach Jominy (+HL)
~ 1,5 mm	49 - 57 HRC	52 - 57 HRC	49 - 54 HRC
~ 3 mm	49 - 57 HRC	52 - 57 HRC	49 - 54 HRC
~ 5 mm	48 - 57 HRC	51 - 57 HRC	48 - 54 HRC
~ 7 mm	45 - 56 HRC	49 - 56 HRC	45 - 52 HRC
~ 9 mm	42 - 55 HRC	46 - 55 HRC	42 - 51 HRC
~ 11 mm	39 - 54 HRC	44 - 54 HRC	39 - 49 HRC
~ 13 mm	36 - 53 HRC	42 - 53 HRC	36 - 47 HRC
~ 15 mm	34 - 52 HRC	40 - 52 HRC	34 - 46 HRC
~ 20 mm	30 - 48 HRC	36 - 48 HRC	30 - 42 HRC
~ 25 mm	28 - 45 HRC	34 - 45 HRC	28 - 39 HRC
~ 30 mm	27 - 43 HRC	32 - 43 HRC	27 - 38 HRC
~ 35 mm	26 - 41 HRC	31 - 41 HRC	26 - 36 HRC
~ 40 mm	25 - 40 HRC	30 - 40 HRC	25 - 35 HRC
~ 45 mm	24 - 40 HRC	29 - 40 HRC	24 - 35 HRC
~ 50 mm	24 - 39 HRC	29 - 39 HRC	24 - 34 HRC

vergütet	Streckgrenze (Re)	Zugfestigkeit (Rm)	Bruchdehnung (A5, 65)	Einschnürung (Z)	Kerbschlagarbeit KV (ISO-V/Charpy-V)	bei Temperatur
<= 16 mm	>= 800 N/mm²	1.000 - 1.200 N/mm²	>= 11 %	>= 45 %		~ 20 ° C
16 - 40 mm	>= 650 N/mm²	900 - 1.100 N/mm²	>= 12 %	>= 50 %	>= 40 Joule	~ 20 ° C
40 - 100 mm	>= 550 N/mm²	800 - 950 N/mm²	>= 14 %	>= 55 %	>= 45 Joule	~ 20 ° C
100 - 160 mm	>= 500 N/mm²	750 - 900 N/mm²	>= 15 %	>= 55 %	>= 45 Joule	~ 20 ° C
160 - 250 mm	>= 450 N/mm²	700 - 850 N/mm²	>= 15 %	>= 60 %	>= 45 Joule	~ 20 ° C

behandelt auf Scherbarkeit

Härte [HBW]

<= 255 HBW

Flacherzeugnisse
vergütet	Streckgrenze (Re)	Zugfestigkeit (Rm)	Bruchdehnung (A5, 65)	Einschnürung (Z)	Kerbschlagarbeit KV (ISO-V/Charpy-V)	bei Temperatur
<= 8 mm	>= 800 N/mm²	1.000 - 1.200 N/mm²	>= 11 %	>= 45 %		~ 20 ° C
8 - 20 mm	>= 650 N/mm²	900 - 1.100 N/mm²	>= 12 %	>= 50 %	>= 40 Joule	~ 20 ° C
20 - 60 mm	>= 550 N/mm²	800 - 950 N/mm²	>= 14 %	>= 55 %	>= 45 Joule	~ 20 ° C
60 - 100 mm	>= 500 N/mm²	750 - 900 N/mm²	>= 15 %	>= 55 %	>= 45 Joule	~ 20 ° C
100 - 160 mm	>= 450 N/mm²	700 - 850 N/mm²	>= 15 %	>= 60 %	>= 45 Joule	~ 20 ° C