![[Translate to Spanish:]](/fileadmin/bilder/slider/Werkstoffe/basedo_stahlrohre_werkstoffe.jpg "[Translate to Spanish:]")
![[Translate to Spanish:]](/fileadmin/bilder/slider/Werkstoffe/HeaderWerkstoffe.jpg "[Translate to Spanish:]")
![[Translate to Spanish:]](/fileadmin/bilder/slider/Werkstoffe/HeaderWerkstoffe2.jpg "[Translate to Spanish:]")
![[Translate to Spanish:]](/fileadmin/bilder/slider/Werkstoffe/HeaderWerkstoffe3.jpg "[Translate to Spanish:]")
![[Translate to Spanish:]](/fileadmin/bilder/slider/Werkstoffe/HeaderWerkstoffe4.jpg "[Translate to Spanish:]")
Material 1.5026
Resorte de acero
Do you have any questions about the material or would you like to order? Complete our inquiry form, it`s free of charge and without obligation. We will get in touch with you in order to provide you with more information.
Standards
Material Category: Resorte de acero
Applications
Resortes helicoidales, placas de resorte, resortes de disco
Heat Treatment
Endurecimiento 850 - 870 C°, aceite refrigerante
Templado 440 - 460 C°
Prueba de enfriamiento frontal 845 - 855 C°
Chemical Composition
| C % | Si % | Mn % | P % | S % | Cr % | Mo % | Ni % | |
| 0,52 - 0,60 | 1,60 - 2,00 | 0,60 - 0,90 | max 0,025 | max 0,025 | max 0,40 | max 0,10 | max 0,40 | Cu+10Sn <= 0,60 |
Product Specifications
DIN EN 10089 (04/2003)
DIN EN 10132-4 (04/2003)
Mechanical Properties
| ~DIN EN 10089 Warmgewalzte Stähle für vergütbare Federn | Härte |
| weichgeglüht | <= 248 HB |
| abgeschreckt | |
| Stirnabschreckversuch nach Jominy | |
| ~ 2,2 mm | ~ 56 HRC |
| ~ 3,5 mm | ~ 56 HRC |
| ~ 4 mm | ~ 52 HRC |
| ~ 5,3 mm | ~ 52 HRC |
| Stirnabschreckversuch nach Jominy (+H) | |
| ~ 1,5 mm | 57 - 65 HRC |
| ~ 3 mm | 55 - 62 HRC |
| ~ 5 mm | 49 - 60 HRC |
| ~ 7 mm | 43 - 57 HRC |
| ~ 9 mm | 37 - 54 HRC |
| ~ 11 mm | 34 - 50 HRC |
| ~ 13 mm | 32 - 46 HRC |
| ~ 15 mm | 31 - 42 HRC |
| ~ 20 mm | 28 - 39 HRC |
| ~ 25 mm | 27 - 37 HRC |
| ~ 30 mm | 26 - 36 HRC |
| ~ 35 mm | 26 - 35 HRC |
| ~ 40 mm | 25 - 34 HRC |
| ~ 45 mm | 25 - 34 HRC |
| ~ 50 mm | 24 - 33 HRC |
| Stirnabschreckversuch nach Jominy (+HH) | |
| ~ 1,5 mm | 60 - 65 HRC |
| ~ 3 mm | 57 - 62 HRC |
| ~ 5 mm | 53 - 60 HRC |
| ~ 7 mm | 48 - 57 HRC |
| ~ 9 mm | 43 - 54 HRC |
| ~ 11 mm | 39 - 50 HRC |
| ~ 13 mm | 37 - 46 HRC |
| ~ 15 mm | 35 - 42 HRC |
| ~ 20 mm | 32 - 39 HRC |
| ~ 25 mm | 30 - 37 HRC |
| ~ 30 mm | 29 - 36 HRC |
| ~ 35 mm | 29 - 35 HRC |
| ~ 40 mm | 28 - 34 HRC |
| ~ 45 mm | 28 - 34 HRC |
| ~ 50 mm | 27 - 33 HRC |
| vergütet | ||||
| 0,2% Dehngrenze (Rp0,2) | Zugfestigkeit (Rm) | Bruchdehnung (A5, 65) | Einschnürung (Z) | Kerbschlagarbeit KU (ISO-U/Charpy-U) |
| >= 1.300 N/mm² | 1.450 - 1.750 N/mm² | >= 6 % | >= 25 % | >= 13 Joule |
| behandelt auf Kaltscherbarkeit | Härte [HB] | <= 280 HB |
| geglüht zur Erzielung kugeliger Carbide | Härte [HB] | <= 230 HB |