![[Translate to Spanish:]](/fileadmin/bilder/slider/Werkstoffe/basedo_stahlrohre_werkstoffe.jpg "[Translate to Spanish:]")
![[Translate to Spanish:]](/fileadmin/bilder/slider/Werkstoffe/HeaderWerkstoffe.jpg "[Translate to Spanish:]")
![[Translate to Spanish:]](/fileadmin/bilder/slider/Werkstoffe/HeaderWerkstoffe2.jpg "[Translate to Spanish:]")
![[Translate to Spanish:]](/fileadmin/bilder/slider/Werkstoffe/HeaderWerkstoffe3.jpg "[Translate to Spanish:]")
![[Translate to Spanish:]](/fileadmin/bilder/slider/Werkstoffe/HeaderWerkstoffe4.jpg "[Translate to Spanish:]")
Material 1.4311
Acero resistente bajo cero
El grado 1.4311 es un acero inoxidable austenítico aleado con nitrógeno.
Do you have any questions about the material or would you like to order? Complete our inquiry form, it`s free of charge and without obligation. We will get in touch with you in order to provide you with more information.
Standards
| HDIN / EN | US-Standard | AFNOR | UNI | JIS | request |
|---|---|---|---|---|---|
| X2CrNiN18-10 | request |
Material Category: Acero resistente bajo cero
Chemical Composition
| C % | Si % | Mn % | P % | S % | Cr % | N % | Ni % |
| max 0,03 | max 1,00 | max 2,00 | max 0,045 | max 0,015 | 17,50 - 19,50 | 0,120 - 0,220 | 8,50 - 11,50 |
Mechanical Properties
| DIN EN 10088-3 (12/2014) Nichtrostende Stähle. Halbzeug, Stäbe, Walzdraht, gezogener Draht, Profile und Blankstahlerzeugnisse aus korrosionsbeständigen Stählen für allgemeine Verwendung. | |||||||
| Stäbe | |||||||
| lösungsgeglüht | 0,2% Dehngrenze (Rp0,2) / bei Temperatur | 1% Dehngrenze (Rp1,0) / bei Temperatur | Zugfestigkeit (Rm) | Bruchdehnung (A 5,65) | Härte [HBW] | Kerbschlagarbeit KV2 (ISO-V/Charpy-V) | Probenlage |
| 160 - 250 mm | >= 270 N/mm² / ~ 20 ° C | >= 305 N/mm² / ~ 20 ° C | 550 - 760 N/mm² | >= 30 % | <= 230 HBW | >= 60 Joule | quer |
| <= 160 mm | >= 270 N/mm² / ~ 20 ° C | >= 305 N/mm² / ~ 20 ° C | 550 - 760 N/mm² | >= 40 % | <= 230 HBW | >= 100 Joule | längs |
| >= 118 N/mm² / ~ 550 ° C | >= 147 N/mm² / ~ 550 ° C | ||||||
| >= 119 N/mm² / ~ 500 ° C | >= 149 N/mm² / ~ 500 ° C | ||||||
| >= 121 N/mm² / ~ 450 ° C | >= 152 N/mm² / ~ 450 ° C | ||||||
| >= 125 N/mm² / ~ 400 ° C | >= 156 N/mm² / ~ 400 ° C | ||||||
| >= 130 N/mm² / ~ 350 ° C | >= 160 N/mm² / ~ 350 ° C | ||||||
| >= 136 N/mm² / ~ 300 ° C | >= 167 N/mm² / ~ 300 ° C | ||||||
| >= 145 N/mm² / ~ 250 ° C | >= 175 N/mm² / ~ 250 ° C | ||||||
| >= 157 N/mm² / ~ 200 ° C | >= 187 N/mm² / ~ 200 ° C | ||||||
| >= 175 N/mm² / ~ 150 ° C | >= 210 N/mm² / ~ 150 ° C | ||||||
| >= 205 N/mm² / ~ 100 ° C | >= 240 N/mm² / ~ 100 ° C | ||||||
| kaltverformt | Zugfestigkeit (Rm) | Bruchdehnung (A5, 65) | Härte [HBW] | Probenlage | bei Temperatur |
| <= 35 mm | 750 - 960 N/mm² | >= 20 % | <= 330 HBW | längs | ~ 20 ° C |
| warmgeformt | Zugfestigkeit (Rm) | Bruchdehnung (A5, 65) | Härte [HBW] | Probenlage | bei Temperatur |
| <= 8 mm | 750 - 960 N/mm² | >= 20 % | <= 330 HBW | längs | ~ 20 ° C |
| Halbzeug | |||||||
| lösungsgeglüht | 0,2% Dehngrenze (Rp0,2) / bei Temperatur | 1% Dehngrenze (Rp1,0) / bei Temperatur | Zugfestigkeit (Rm) | Bruchdehnung (A 5,65) | Härte [HBW] | Kerbschlagarbeit KV2 (ISO-V/Charpy-V) | Probenlage |
| 160 - 250 mm | >= 270 N/mm² / ~ 20 ° C | >= 305 N/mm² / ~ 20 ° C | 550 - 760 N/mm² | >= 30 % | <= 230 HBW | >= 60 Joule | quer |
| <= 160 mm | >= 270 N/mm² / ~ 20 ° C | >= 305 N/mm² / ~ 20 ° C | 550 - 760 N/mm² | >= 40 % | <= 230 HBW | >= 100 Joule | längs |
| >= 118 N/mm² / ~ 550 ° C | >= 147 N/mm² / ~ 550 ° C | ||||||
| >= 119 N/mm² / ~ 500 ° C | >= 149 N/mm² / ~ 500 ° C | ||||||
| >= 121 N/mm² / ~ 450 ° C | >= 152 N/mm² / ~ 450 ° C | ||||||
| >= 125 N/mm² / ~ 400 ° C | >= 156 N/mm² / ~ 400 ° C | ||||||
| >= 130 N/mm² / ~ 350 ° C | >= 160 N/mm² / ~ 350 ° C | ||||||
| >= 136 N/mm² / ~ 300 ° C | >= 167 N/mm² / ~ 300 ° C | ||||||
| >= 145 N/mm² / ~ 250 ° C | >= 175 N/mm² / ~ 250 ° C | ||||||
| >= 157 N/mm² / ~ 200 ° C | >= 187 N/mm² / ~ 200 ° C | ||||||
| >= 175 N/mm² / ~ 150 ° C | >= 210 N/mm² / ~ 150 ° C | ||||||
| >= 205 N/mm² / ~ 100 ° C | >= 240 N/mm² / ~ 100 ° C | ||||||
| Walzdraht | ||
| lösungsgeglüht | Zugfestigkeit (Rm) | bei Temperatur |
| <= 160 mm | 750 - 960 N/mm² | ~ 20 ° C |
| 160 - 250 mm | 550 - 760 N/mm² | ~ 20 ° C |
| Gezogener Draht | |||||||
| lösungsgeglüht | 0,2% Dehngrenze (Rp0,2) / bei Temperatur | 1% Dehngrenze (Rp1,0) / bei Temperatur | Zugfestigkeit (Rm) | Bruchdehnung (A 5,65) | Härte [HBW] | Kerbschlagarbeit KV2 (ISO-V/Charpy-V) | Probenlage |
| 160 - 250 mm | >= 270 N/mm² / ~ 20 ° C | >= 305 N/mm² / ~ 20 ° C | 550 - 760 N/mm² | >= 30 % | <= 230 HBW | >= 60 Joule | quer |
| <= 160 mm | >= 270 N/mm² / ~ 20 ° C | >= 305 N/mm² / ~ 20 ° C | 550 - 760 N/mm² | >= 40 % | <= 230 HBW | >= 100 Joule | längs |
| >= 118 N/mm² / ~ 550 ° C | >= 147 N/mm² / ~ 550 ° C | ||||||
| >= 119 N/mm² / ~ 500 ° C | >= 149 N/mm² / ~ 500 ° C | ||||||
| >= 121 N/mm² / ~ 450 ° C | >= 152 N/mm² / ~ 450 ° C | ||||||
| >= 125 N/mm² / ~ 400 ° C | >= 156 N/mm² / ~ 400 ° C | ||||||
| >= 130 N/mm² / ~ 350 ° C | >= 160 N/mm² / ~ 350 ° C | ||||||
| >= 136 N/mm² / ~ 300 ° C | >= 167 N/mm² / ~ 300 ° C | ||||||
| >= 145 N/mm² / ~ 250 ° C | >= 175 N/mm² / ~ 250 ° C | ||||||
| >= 157 N/mm² / ~ 200 ° C | >= 187 N/mm² / ~ 200 ° C | ||||||
| >= 175 N/mm² / ~ 150 ° C | >= 210 N/mm² / ~ 150 ° C | ||||||
| >= 205 N/mm² / ~ 100 ° C | >= 240 N/mm² / ~ 100 ° C | ||||||
| Profile | |||||||
| lösungsgeglüht | 0,2% Dehngrenze (Rp0,2) / bei Temperatur | 1% Dehngrenze (Rp1,0) / bei Temperatur | Zugfestigkeit (Rm) | Bruchdehnung (A 5,65) | Härte [HBW] | Kerbschlagarbeit KV2 (ISO-V/Charpy-V) | Probenlage |
| 160 - 250 mm | >= 270 N/mm² / ~ 20 ° C | >= 305 N/mm² / ~ 20 ° C | 550 - 760 N/mm² | >= 30 % | <= 230 HBW | >= 60 Joule | quer |
| <= 160 mm | >= 270 N/mm² / ~ 20 ° C | >= 305 N/mm² / ~ 20 ° C | 550 - 760 N/mm² | >= 40 % | <= 230 HBW | >= 100 Joule | längs |
| >= 118 N/mm² / ~ 550 ° C | >= 147 N/mm² / ~ 550 ° C | ||||||
| >= 119 N/mm² / ~ 500 ° C | >= 149 N/mm² / ~ 500 ° C | ||||||
| >= 121 N/mm² / ~ 450 ° C | >= 152 N/mm² / ~ 450 ° C | ||||||
| >= 125 N/mm² / ~ 400 ° C | >= 156 N/mm² / ~ 400 ° C | ||||||
| >= 130 N/mm² / ~ 350 ° C | >= 160 N/mm² / ~ 350 ° C | ||||||
| >= 136 N/mm² / ~ 300 ° C | >= 167 N/mm² / ~ 300 ° C | ||||||
| >= 145 N/mm² / ~ 250 ° C | >= 175 N/mm² / ~ 250 ° C | ||||||
| >= 157 N/mm² / ~ 200 ° C | >= 187 N/mm² / ~ 200 ° C | ||||||
| >= 175 N/mm² / ~ 150 ° C | >= 210 N/mm² / ~ 150 ° C | ||||||
| >= 205 N/mm² / ~ 100 ° C | >= 240 N/mm² / ~ 100 ° C | ||||||
| kaltverformt | Zugfestigkeit (Rm) | Bruchdehnung (A5, 65) | Härte [HBW] | Probenlage | bei Temperatur |
| <= 35 mm | 750 - 960 N/mm² | >= 20 % | <= 330 HBW | längs | ~ 20 ° C |
| warmgeformt | Zugfestigkeit (Rm) | Bruchdehnung (A5, 65) | Härte [HBW] | Probenlage | bei Temperatur |
| <= 8 mm | 750 - 960 N/mm² | >= 20 % | <= 330 HBW | längs | ~ 20 ° C |