![[Translate to Spanish:]](/fileadmin/bilder/slider/Werkstoffe/basedo_stahlrohre_werkstoffe.jpg "[Translate to Spanish:]")
![[Translate to Spanish:]](/fileadmin/bilder/slider/Werkstoffe/HeaderWerkstoffe.jpg "[Translate to Spanish:]")
![[Translate to Spanish:]](/fileadmin/bilder/slider/Werkstoffe/HeaderWerkstoffe2.jpg "[Translate to Spanish:]")
![[Translate to Spanish:]](/fileadmin/bilder/slider/Werkstoffe/HeaderWerkstoffe3.jpg "[Translate to Spanish:]")
![[Translate to Spanish:]](/fileadmin/bilder/slider/Werkstoffe/HeaderWerkstoffe4.jpg "[Translate to Spanish:]")
Material 1.1141
acero endurecido
El material C 15E es un acero de cementación. Este material se utiliza para la construcción de bajo estrés y piezas de maquinaria. El material se puede cementar y es fácil de mecanizar y soldar.
Do you have any questions about the material or would you like to order? Complete our inquiry form, it`s free of charge and without obligation. We will get in touch with you in order to provide you with more information.
Standards
| HDIN / EN | US-Standard | AFNOR | UNI | JIS | request |
|---|---|---|---|---|---|
| C15E/Ck15 C15 | AISI 1020 UNS G10200 | 1C15 | S15C S15CK | request |
Material Category: acero endurecido
Applications
Ingeniería general
construcción de contenedores
Heat Treatment
Temperatura de cementación 880 - 980 C°, refrigeración por aceite/agua
Temperatura de endurecimiento del núcleo 880 - 920 C°, aceite refrigerante / agua
Temperatura de endurecimiento superficial 780 - 820 C°, refrigeración por aceite
Templado 150 - 200 C°, mínimo 1 hora, enfriamiento al aire
Weldability
El material C15E es fácil de soldar.
Chemical Composition
| C % | Si % | Mn % | P % | S % |
| 0,12 - 0,18 | max 0,40 | 0,30 - 0,60 | max 0,035 | max 0,035 |
Product Specifications
DIN EN 10084
DIN EN 10132-2
DIN EN 10277
DIN EN 10297-1
DIN EN ISO 683-3
Mechanical Properties
| 1.1141 / C15E | |||
| Härte HBW | |||
| Normalgeglüht | 95 - 150 HBW | ||
| Weichgeglüht | max 143 HBW | ||
| Vergütet bei ~ 200 C° | Zugfestigkeit RM | ||
| <= 16 mm | >= 800 N/mm² | ||
| 16 - 40 mm | >= 600 N/mm² | ||
| Gewalzt und geschält EN 10277 | Zugfestigkeit RM | ||
| 16 - 40 mm | 330 - 600 N/mm² | ||
| 40 - 63 mm | 330 - 600 N/mm² | ||
| 63 - 100 mm | 330 - 600 N/mm² | ||
| Härte HBW | |||
| 16 - 40 mm | 98 - 178 HBW | ||
| 40 - 63 mm | 98 - 178 HBW | ||
| 63 - 100 mm | 98 - 178 HBW | ||
| Weichgeglüht und geschält | Härte HBW | ||
| 16 - 40 mm | max 143 HBW | ||
| 40 - 63 mm | max 143 HBW | ||
| 63 - 100 mm | max 143 HBW | ||
| Kaltgezogen | Zugfestigkeit Rm | Dehngrenze Rp 0,2 | Bruchdehnung A5 % |
| 5 - 10 mm | 500 - 800 N/mm² | >= 380 N/mm² | >= 7 % |
| 10 - 16 mm | 480 - 780 N/mm² | >=340 N/mm² | >= 8 % |
| 16 - 40 mm | 430 - 730 N/mm² | >= 280 N/mm² | >= 9 % |
| 40 - 63 mm | 380 - 670 N/mm² | >= 240 N/mm² | >= 11 % |
| 63 - 100 mm | 340 - 600 N/mm² | >= 215 N/mm² | >= 12 % |