![[Translate to Spanish:]](/fileadmin/bilder/slider/Werkstoffe/basedo_stahlrohre_werkstoffe.jpg "[Translate to Spanish:]")
![[Translate to Spanish:]](/fileadmin/bilder/slider/Werkstoffe/HeaderWerkstoffe.jpg "[Translate to Spanish:]")
![[Translate to Spanish:]](/fileadmin/bilder/slider/Werkstoffe/HeaderWerkstoffe2.jpg "[Translate to Spanish:]")
![[Translate to Spanish:]](/fileadmin/bilder/slider/Werkstoffe/HeaderWerkstoffe3.jpg "[Translate to Spanish:]")
![[Translate to Spanish:]](/fileadmin/bilder/slider/Werkstoffe/HeaderWerkstoffe4.jpg "[Translate to Spanish:]")
Material 1.0757
acero de corte libre
El material 46SPb20 es un acero de corte libre eliminado con silicio. La adición de plomo hace que el material sea fácil de mecanizar. 46SPb20 se puede templar.
Do you have any questions about the material or would you like to order? Complete our inquiry form, it`s free of charge and without obligation. We will get in touch with you in order to provide you with more information.
Standards
Material Category: acero de corte libre
Heat Treatment
Temple 840 - 870 C°, Temple agua o aceite, duración >= 30 minutos
Templado 540 - 680 C°, duración >= 1 hora
Weldability
El material 46SPb20 no debe soldarse.
Chemical Composition
| C % | Si % | Mn % | P % | S % | Pb % |
| 0,42 - 0,50 | max 0,40 | 0,70 - 1,10 | max 0,060 | 0,150 - 0,250 | 0,150 - 0,350 |
Product Specifications
DIN EN 10277
DIN EN 683-4
Mechanical Properties
| 1.0757 / 46SPb20 Blankstahlerzeugnisse. Automatenstähle. Vergütungsstähle. gewalzt und geschält | |||
| Abmessung (mm) | Zugfestigkeit (Rm) | Härte (HBW) | |
| 16 - 40 mm | 590 - 760 N/mm² | <= 222 HBW | |
| 40 - 63 mm | 580 - 730 N/mm² | <= 213 HBW | |
| 63 - 100 mm | 560 - 710 N/mm² | <= 207 HBW | |
| vergütet und geschält | 0,2% Dehngrenze (Rp0,2) | Zugfestigkeit (Rm) | Bruchdehnung (A5,65) |
| 16 - 40 mm | >= 430 N/mm² | 650 - 800 N/mm² | >= 13 % |
| 40 - 63 mm | >= 370 N/mm² | 630 - 780 N/mm2 | >= 14 % |
| 63 - 100 mm | >= 370 N/mm² | 630 - 780 N/mm² | >= 14 % |
| kaltgezogen und vergütet | 0,2% Dehngrenze (Rp0,2) | Zugfestigkeit (Rm) | Bruchdehnung (A5, 65) |
| 16 - 40 mm | >= 430 N/mm² | 650 - 800 N/mm² | >= 13 % |
| 40 - 63 mm | >= 370 N/mm² | 630 - 780 N/mm² | >= 14 % |
| 63 - 100 mm | >= 370 N/mm² | 630 - 780 N/mm² | >= 14 % |
| kaltgezogen | 0,2% Dehngrenze (Rp0,2) | Zugfestigkeit (Rm) | Bruchdehnung (A5, 65) |
| 5 - 10 mm | >=570 N/mm² | 740 - 980 N/mm² | >= 5 % |
| 10 - 16 mm | >= 470 N/mm2 | 690 - 930 N/mm² | >= 6 % |
| 16 - 40 mm | >= 400 N/mm² | 640 - 880 N/mm² | >= 7 % |
| 40 - 63 mm | >= 380 N/mm2 | 610 - 850 N/mm² | >= 8 % |
| 63 - 100 mm | >= 340 N/mm2 | 580 - 820 N/mm² | >= 8 % |
| vergütet und kaltgezogen | 0,2% Dehngrenze (Rp0,2) | Zugfestigkeit (Rm) | Bruchdehnung (A5, 65) |
| 5 - 10 mm | >= 595 N/mm² | 850 - 1000 N/mm² | >= 8 % |
| 10 - 16 mm | >= 560 N/mm² | 800 -950 N/mm² | >= 9 % |
| 16 - 40 mm | >= 490 N/mm² | 700 - 850 N/mm² | >= 10 % |
| 40 - 63 mm | >= 490 N/mm2 | 700 -850 N/mm2 | >= 11 % |
| 63 - 100 mm | >= 455 N/mm2 | 650 - 850 N/mm² | >= 11 % |