Material 1.8937

Feinkornbaustahl

Do you have any questions about the material or would you like to order? Complete our inquiry form, it`s free of charge and without obligation. We will get in touch with you in order to provide you with more information.

Standards

HDIN / EN	US-Standard	AFNOR	UNI	JIS	request
P500NH WStE500					request

Material Category: Feinkornbaustahl

Chemical Composition

C %

Si %

Mn %

P %

S %

Al %

Cr %

Cu %

Mo %

N %

Nb %

Ni %

Ti %

V %

max 0,21

0,10 - 0,60

1,00 - 1,70

max 0,035

max 0,030

mind 0,0200

max 0,30

max 0,70

max 0,10

max 0,020

max 0,050

max 1,00

max 0,20

max 0,22

Mechanical Properties

Abmessung	Streckgrenze (Re)	Zugfestigkeit (Rm)	Bruchdehnung (A5, 65)	Faltversucht
<= 16 mm	>= 500 N/mm²
16 - 35 mm	>= 480 N/mm²
35 - 50 mm	>= 470 N/mm²
50 - 60 mm	>= 460 N/mm²
60 - 70 mm	>= 450 N/mm²
>= 70 mm			~ 16 %
<= 70 mm		610 - 780 N/mm²	~ 16 %
70 - 85 mm	>= 440 N/mm²	600 - 770 N/mm²
85 - 100 mm	>= 430 N/mm²	590 - 760 N/mm²
100 - 125 mm	>= 420 N/mm²	580 - 750 N/mm²
125 - 150 mm	>= 410 N/mm²	570 - 740 N/mm²
150 - 250 mm	>= 400 N/mm²	560 - 740 N/mm²
<= 250 mm				längs

0,2% Dehngrenze (Rp0,2)	Wert	bei Temperatur
<= 35 mm	>= 422 N/mm²	~ 100 ° C
<= 35 mm	>= 392 N/mm²	~ 150 ° C
<= 70 mm	>= 363 N/mm²	~ 200 ° C
<= 70 mm	>= 333 N/mm²	~ 250 ° C
<= 70 mm	>= 314 N/mm²	~ 300 ° C
<= 70 mm	>= 284 N/mm²	~ 350 ° C
<= 70 mm	>= 255 N/mm²	~ 400 ° C
35 - 70 mm	>= 412 N/mm²	~ 100 ° C
35 - 70 mm	>= 382 N/mm²	~ 150 ° C
70 - 85 mm	>= 402 N/mm²	~ 100 ° C
70 - 85 mm	>= 373 N/mm²	~ 150 ° C
70 - 85 mm	>= 353 N/mm²	~ 200 ° C
70 - 85 mm	>= 324 N/mm²	~ 250 ° C
70 - 85 mm	>= 304 N/mm²	~ 300 ° C
70 - 85 mm	>= 275 N/mm²	~ 350 ° C
70 - 85 mm	>= 245 N/mm²	~ 400 ° C
85 - 100 mm	>= 392 N/mm²	~ 100 ° C
85 - 100 mm	>= 363 N/mm²	~ 150 ° C
85 - 100 mm	>= 343 N/mm²	~ 200 ° C
85 - 100 mm	>= 314 N/mm²	~ 250 ° C
85 - 100 mm	>= 294 N/mm²	~ 300 ° C
85 - 100 mm	>= 265 N/mm²	~ 350 ° C
85 - 100 mm	>= 235 N/mm²	~ 400 ° C
100 - 125 mm	>= 382 N/mm²	~ 100 ° C
100 - 125 mm	>= 353 N/mm²	~ 150 ° C
100 - 125 mm	>= 333 N/mm²	~ 200 ° C
100 - 125 mm	>= 304 N/mm²	~ 250 ° C
100 - 125 mm	>= 284 N/mm²	~ 300 ° C
100 - 125 mm	>= 255 N/mm²	~ 350 ° C
100 - 125 mm	>= 226 N/mm²	~ 400 ° C
125 - 150 mm	>= 373 N/mm²	~ 100 ° C
125 - 150 mm	>= 343 N/mm²	~ 150 ° C
125 - 150 mm	>= 324 N/mm²	~ 200 ° C
125 - 150 mm	>= 294 N/mm²	~ 250 ° C
125 - 150 mm	>= 275 N/mm²	~ 300 ° C
125 - 150 mm	>= 245 N/mm²	~ 350 ° C
125 - 150 mm	>= 216 N/mm²	~ 400 ° C
150 - 250 mm	>= 363 N/mm²	~ 100 ° C
150 - 250 mm	>= 333 N/mm²	~ 150 ° C
150 - 250 mm	>= 314 N/mm²	~ 200 ° C
150 - 250 mm	>= 284 N/mm²	~ 250 ° C
150 - 250 mm	>= 265 N/mm²	~ 300 ° C
150 - 250 mm	>= 235 N/mm²	~ 350 ° C
150 - 250 mm	>= 206 N/mm²	~ 400 ° C

normalgeglüht	Kerbschlagarbeit KV (ISO-V/Charpy-V)	Probenlage	bei Temperatur
10 - 150 mm	~ 40 Joule	längs	~ -20 ° C
10 - 150 mm	~ 20 Joule	quer	~ -20 ° C
10 - 150 mm	~ 43 Joule	längs	~ -10 ° C
10 - 150 mm	~ 24 Joule	quer	~ -10 ° C
10 - 150 mm	~ 47 Joule	längs	~ 0 ° C
10 - 150 mm	~ 27 Joule	quer	~ 0 ° C
10 - 150 mm	~ 51 Joule	längs	~ 10 ° C
10 - 150 mm	~ 31 Joule	quer	~ 10 ° C
10 - 150 mm	~ 55 Joule	längs	~ 20 ° C
10 - 150 mm	~ 31 Joule	quer	~ 20 ° C