Material 1.7225

Vergütungsstahl

Do you have any questions about the material or would you like to order? Complete our inquiry form, it`s free of charge and without obligation. We will get in touch with you in order to provide you with more information.

Standards

HDIN / EN	US-Standard	AFNOR	UNI	JIS	request
42CrMo4	AISI 4140 AISI 4140H AISI 4140RH AISI 4142 AISI 4142H AISI 4145 UNS G41400 UNS G41420 UNS G41450 UNS H41400 UNS H41420 UNS K14248		38CrMo4KB 41CrMo4	SCM440 SCM440H SCMHRCH SCM440M SCM440RCH SCM440TK SCM440WCH SNB7Class2	request

Material Category: Vergütungsstahl

Chemical Composition

C %	Si %	Mn %	P %	S %	Cr %	Mo %
0,38 - 0,45	max 0,40	0,60 - 0,90	max 0,025	max 0,035	0,90 - 1,20	0,15 - 0,30

Product Specifications

DIN EN 10083-3 (01/2007)
DIN EN 10132-3 (05/2000)
DIN EN 10250-3 (12/1999)
DIN EN 10263-4 (02/2018)
DIN EN 10269 (02/2014)
DIN EN 10277 (09/2018)
DIN EN 10297-1 (06/2003)
DIN EN 10305-1 (08/2016)
DIN EN 10343 (07/2009)
DIN EN ISO 683-2 (09/2018)
DIN SEW 310 (08/1992)
DIN SEW 550 (08/1976)

Mechanical Properties

DIN EN 10083-3 (01/2007) Vergütungsstähle. Legierte Stähle.
weichgeglüht	Härte [HBW]	<= 223 HBW

Oberflächenhärte [HRC]
<= 250 mm	>= 53 HRC

abgeschreckt	Stirnabschreckversuch nach Jominy (+H)	Stirnabschreckversuch nach Jominy (+HH)	Stirnabschreckversuch nach Jominy (+HL)
~ 1,5 mm	53 - 61 HRC	56 - 61 HRC	53 - 58 HRC
~ 3 mm	53 - 61 HRC	56 - 61 HRC	53 - 58 HRC
~ 5 mm	52 - 61 HRC	55 - 61 HRC	52 - 58 HRC
~ 7 mm	51 - 60 HRC	54 - 60 HRC	51 - 57 HRC
~ 9 mm	49 - 60 HRC	52 - 60 HRC	49 - 56 HRC
~ 11 mm	43 - 59 HRC	48 - 59 HRC	43 - 54 HRC
~ 13 mm	40 - 59 HRC	46 - 59 HRC	40 - 53 HRC
~ 15 mm	37 - 58 HRC	44 - 58 HRC	37 - 51 HRC
~ 20 mm	34 - 56 HRC	41 - 56 HRC	34 - 49 HRC
~ 25 mm	32 - 53 HRC	39 - 53 HRC	32 - 46 HRC
~ 30 mm	31 - 51 HRC	38 - 51 HRC	31 - 44 HRC
~ 35 mm	30 - 48 HRC	36 - 48 HRC	30 - 42 HRC
~ 40 mm	30 - 47 HRC	36 - 47 HRC	30 - 41 HRC
~ 45 mm	29 - 46 HRC	35 - 46 HRC	29 - 40 HRC
~ 50 mm	29 - 45 HRC	34 - 45 HRC	29 - 40 HRC

vergütet	Streckgrenze (Re)	Zugfestigkeit (Rm)	Bruchdehnung (A5, 65)	Einschnürung (Z)	Kerbschlagarbeit KV (ISO-V/Charpy-V)	bei Temperatur
<= 16 mm	>= 900 N/mm²	1.100 - 1.300 N/mm²	>= 10 %	>= 40 %		~ 20 ° C
16 - 40 mm	>= 750 N/mm²	1.000 - 1.200 N/mm²	>= 11 %	>= 45 %	>= 35 Joule	~ 20 ° C
40 - 100 mm	>= 650 N/mm²	900 - 1.100 N/mm²	>= 12 %	>= 50 %	>= 35 Joule	~ 20 ° C
100 - 160 mm	>= 550 N/mm²	800 - 950 N/mm²	>= 13 %	>= 50 %	>= 35 Joule	~ 20 ° C
160 - 250 mm	>= 500 N/mm²	750 - 900 N/mm²	>= 14 %	>= 55 %	>= 35 Joule	~ 20 ° C

behandelt auf Scherbarkeit

Härte [HBW]

<= 255 HBW

Flacherzeugnisse
vergütet	Streckgrenze (Re)	Zugfestigkeit (Rm)	Bruchdehnung (A5, 65)	Einschnürung (Z)	Kerbschlagarbeit KV (ISO-V/Charpy-V)	bei Temperatur
<= 8 mm	>= 800 N/mm²	1.000 - 1.200 N/mm²	>= 11 %	>= 45 %		~ 20 ° C
8 - 20 mm	>= 650 N/mm²	900 - 1.100 N/mm²	>= 12 %	>= 50 %	>= 40 Joule	~ 20 ° C
20 - 60 mm	>= 550 N/mm²	800 - 950 N/mm²	>= 14 %	>= 55 %	>= 45 Joule	~ 20 ° C
60 - 100 mm	>= 500 N/mm²	750 - 900 N/mm²	>= 15 %	>= 55 %	>= 45 Joule	~ 20 ° C
100 - 160 mm	>= 450 N/mm²	700 - 850 N/mm²	>= 15 %	>= 60 %	>= 45 Joule	~ 20 ° C