Material 1.4406

Acero resistente bajo cero

El grado 1.4406 es un acero inoxidable de ferrita.

Do you have any questions about the material or would you like to order? Complete our inquiry form, it`s free of charge and without obligation. We will get in touch with you in order to provide you with more information.

Standards

HDIN / EN	US-Standard	AFNOR	UNI	JIS	request
X2CrNiMoN17-11-2					request

Material Category: Acero resistente bajo cero

Chemical Composition

C %	Si %	Mn %	P %	S %	Cr %	Mo %	N %	Ni %
max 0,03	max 1,00	max 2,00	max 0,045	max 0,015	16,50 - 18,50	2,00 - 2,50	0,120 - 0,220	10,00 - 12,50

Mechanical Properties

0,2% Dehngrenze (Rp0,2)	Zugfestigkeit (Rm)	Bruchdehnung (A5, 65)	Kerbschlagarbeit KV (ISO-V/Charpy-V) / Probenlage	bei Temperatur
~ 785 MPa	>= 1.130 MPa	>= 25 %	>= 60 Joule / quer	~ -195 ° C
~ 390 MPa	>= 780 MPa	>= 30 %		~ -80 ° C

lösungsgeglüht	0,2% Dehngrenze (Rp0,2) / bei Temperatur	1% Dehngrenze (Rp1,0)	Zugfestigkeit (Rm)	Bruchdehnung (A5, 65)	Härte [HB 30]	Kerbschlagarbeit KV (ISO-V/Charpy-V)	Probenlage
<= 160 mm				>= 40 %		>= 100 Joule	längs
160 - 250 mm				>= 30 %		>= 60 Joule	quer
<= 250 mm	>= 280 N/mm²	>= 315 N/mm²	580 - 800 N/mm²		<= 250 HB 30		längs
	>= 136 N/mm² / ~ 550 ° C
	>= 138 N/mm² / ~ 500 ° C
	>= 140 N/mm² / ~ 450 ° C
	>= 145 N/mm² / ~ 400 ° C
	>= 150 N/mm² / ~ 350 ° C
	>= 155 N/mm² / ~ 300 ° C
	>= 165 N/mm² / ~ 250 ° C
	>= 175 N/mm² / ~ 200 ° C
	>= 195 N/mm² / ~ 150 ° C
	>= 215 N/mm² / ~ 100 ° C

abgeschreckt	0,2% Dehngrenze (Rp0,2)	Zugfestigkeit (Rm)	Bruchdehnung (A5, 65)	Einschnürung (Z)	Kerbschlagarbeit KV (ISO-V/Charpy-V)
<= 50 mm	>= 280 N/mm²	580 - 780 N/mm²	>= 40 %	>= 50 %	>= 100 Joule