Material 1.0565

acero estructural de grano fino

El material 1.0565 es un acero estructural de grano fino. Este acero se utiliza a menudo en la construcción de calderas de vapor y recipientes a presión.

Do you have any questions about the material or would you like to order? Complete our inquiry form, it`s free of charge and without obligation. We will get in touch with you in order to provide you with more information.

Standards

HDIN / EN	US-Standard	AFNOR	UNI	JIS	request
P355NH WStE355	ASTM A350LF2ASMESA350LF2 UNS K01600 UNS K02007 UNS K02700 UNS K02701 UNS K02803 UNS K11803 UNS 12001 UNS K12037 UNS K12609		FeE355-2 FeE355KW		request

Material Category: acero estructural de grano fino

Chemical Composition

C %

Si %

Mn %

P %

S %

Al %

Cr %

Cu %

Mo %

N %

Nb %

Ni %

Ti %

V %

max 0,18

max 0,50

1,10 - 1,70

max 0,025

max 0,010

mind 0,0200

max 0,30

max 0,08

max 0,012

max 0,050

max 0,50

max 0,03

max 0,10

Product Specifications

DIN EN 10028-3
DIN EN 10216-3
DIN EN 10217-3
DIN EN 10222-4
DIN EN 10273

Mechanical Properties

Stäbe DIN EN 10273 Warmgewalzte schweißgeeignete Stäbe aus Stahl für Druckbehälter mit festgelegten Eigenschaften bei erhöhten Temperaturen.
Kerbschlagarbeit KV2 (ISO-V/Charpy-V)	Wert	Probenlage	bei Temperatur
	>= 40 Joule	längs	~ -20 ° C
	>= 47 Joule	längs	~ 0 ° C
	>= 55 Joule	längs	~ 20 ° C

normalgeglüht	Streckgrenze (Re)	Zugfestigkeit (Rm)	Bruchdehnung (A5, 65)	Probenlage	bei Temperatur
<= 16 mm	>= 355 N/mm²	490 - 630 MPa	>= 22 %	längs	~ 20 ° C
16 - 35 mm	>= 355 N/mm²	490 - 630 MPa	>= 22 %	längs	~ 20 ° C
35 - 50 mm	>= 345 N/mm²	490 - 630 MPa	>= 22 %	längs	~ 20 ° C
50 - 70 mm	>= 325 N/mm²	490 - 630 MPa	>= 22 %	längs	~ 20 ° C
70 - 100 mm	>= 315 MPa	470 - 610 MPa	>= 21 %	längs	~ 20 ° C
100 - 150 mm	>= 295 MPa	450 - 590 MPa	>= 21 %	längs	~ 20 ° C

0,2% Dehngrenze (Rp0,2)	Wert	bei Temperatur
<= 16 mm	>= 345 MPa	~ 20 ° C
<= 16 mm	>= 343 MPa	~ 50 ° C
<= 16 mm	>= 323 MPa	~ 100 ° C
<= 16 mm	>= 299 MPa	~ 150 ° C
<= 16 mm	>= 275 MPa	~ 200 ° C
<= 16 mm	>= 252 MPa	~ 250 ° C
<= 16 mm	>= 232 MPa	~ 300 ° C
<= 16 mm	>= 214 MPa	~ 350 ° C
<= 16 mm	>= 202 MPa	~ 400 ° C
16 - 35 mm	>= 345 MPa	~ 20 ° C
16 - 40 mm	>= 334 MPa	~ 50 ° C
16 - 40 mm	>= 314 MPa	~ 100 ° C
16 - 40 mm	>= 291 MPa	~ 150 ° C
16 - 40 mm	>= 267 MPa	~ 200 ° C
16 - 40 mm	>= 245 MPa	~ 250 ° C
16 - 40 mm	>= 225 MPa	~ 300 ° C
16 - 40 mm	>= 208 MPa	~ 350 ° C
16 - 40 mm	>= 196 MPa	~ 400 ° C
35 - 50 mm	>= 335 MPa	~ 20 ° C
40 - 60 mm	>= 324 MPa	~ 50 ° C
40 - 60 mm	>= 305 MPa	~ 100 ° C
40 - 60 mm	>= 282 MPa	~ 150 ° C
40 - 60 mm	>= 259 MPa	~ 200 ° C
40 - 60 mm	>= 238 MPa	~ 250 ° C
40 - 60 mm	>= 219 MPa	~ 300 ° C
40 - 60 mm	>= 202 MPa	~ 350 ° C
40 - 60 mm	>= 190 MPa	~ 400 ° C
50 - 70 mm	>= 315 MPa	~ 20 ° C
60 - 100 mm	>= 305 MPa	~ 50 ° C
60 - 100 mm	>= 287 MPa	~ 100 ° C
60 - 100 mm	>= 265 MPa	~ 150 ° C
60 - 100 mm	>= 244 MPa	~ 200 ° C
60 - 100 mm	>= 224 MPa	~ 250 ° C
60 - 100 mm	>= 206 MPa	~ 300 ° C
60 - 100 mm	>= 190 MPa	~ 350 ° C
60 - 100 mm	>= 179 MPa	~ 400 ° C
70 - 100 mm	>= 305 MPa	~ 20 ° C
100 - 150 mm	>= 285 MPa	~ 20 ° C
100 - 150 mm	>= 295 MPa	~ 50 ° C
100 - 150 mm	>= 277 MPa	~ 100 ° C
100 - 150 mm	>= 257 MPa	~ 150 ° C
100 - 150 mm	>= 236 MPa	~ 200 ° C
100 - 150 mm	>= 216 MPa	~ 250 ° C
100 - 150 mm	>= 199 MPa	~ 300 ° C
100 - 150 mm	>= 184 MPa	~ 350 ° C
100 - 150 mm	>= 173 MPa	~ 400 ° C