Material 1.4313

Stainless steel

Grade 1.4313 is a soft-martensitic chrome-nickel stainless steel with additonal molybdenum. It is usually being delivered in quenched and tempered condition. It can be found in the pump as well as in the turbine construction.

Do you have any questions about the material or would you like to order? Complete our inquiry form, it`s free of charge and without obligation. We will get in touch with you in order to provide you with more information.

1.4313

Standards

HDIN / EN US-Standard AFNOR UNI JIS request
X3CrNiMo13-4 4CrNi134 AISI CA6-NM ASTM F6NM UNS S41500 SUSF6NM request

Material Category: Stainless steel

Chemical Composition

C % Si % Mn % P % S %  Cr % Mo % N % Ni %
max 0,05 max 0,70 max 1,50 max 0,040 max 0,015 12,00 - 14,00 0,30 - 0,70 max 0,020 3,50 - 4,50

 

Mechanical Properties

DIN EN 10088-3 (12/2014)
Nichtrostende Stähle. Halbzeug, Stäbe, Walzdraht, gezogener Draht, Profile und Blankstahlerzeugnisse aus korrosionsbeständigen Stählen für allgemeine Verwendung.
Stäbe
geglüht Zugfestigkeit (Rm) Härte [HBW] bei Temperatur
  <= 1.100 N/mm² <= 320 HBW ~ 20 ° C
vergütet 0,2% Dehngrenze (Rp0,2) /
bei Temperatur		 Zugfestigkeit (Rm) Bruchdehnung (A 5,65) Kerbschlagarbeit KV2
(ISO-V/Charpy-V)		 Probenlage
160 - 250 mm >= 800 N/mm² / ~ 20 ° C 900 - 1.100 N/mm² >= 12 % >= 50 Joule quer
160 - 250 mm >= 620 N/mm² / ~ 20 ° C 780 - 980 N/mm² >= 12 % >= 70 Joule quer
160 - 250 mm >= 520 N/mm² / ~ 20 ° C 700 - 850 N/mm² >= 10 % >= 70 Joule quer
<= 160 mm >= 800 N/mm² / ~ 20 ° C 900 - 1.100 N/mm² >= 15 % >= 40 Joule längs
<= 160 mm >= 620 N/mm² / ~ 20 ° C 780 - 980 N/mm² >= 15 % >= 50 Joule längs
<= 160 mm >= 520 N/mm² / ~ 20 ° C 700 - 850 N/mm² >= 12 % >= 50 Joule längs
  >= 515 N/mm² / ~ 350 ° C        
  >= 450 N/mm² / ~ 350 ° C        
  >= 620 N/mm² / ~ 300 ° C        
  >= 530 N/mm² / ~ 300 ° C        
  >= 460 N/mm² / ~ 300 ° C        
  >= 640 N/mm² / ~ 250 ° C        
  >= 545 N/mm² / ~ 250 ° C        
  >= 470 N/mm² / ~ 250 ° C        
  >= 665 N/mm² / ~ 200 ° C        
  >= 560 N/mm² / ~ 200 ° C        
  >= 480 N/mm² / ~ 200 ° C        
  >= 690 N/mm² / ~ 150 ° C        
  >= 575 N/mm² / ~ 150 ° C        
  >= 490 N/mm² / ~ 150 ° C        
  >= 720 N/mm² / ~ 100 ° C        
  >= 590 N/mm² / ~ 100 ° C        
  >= 500 N/mm² / ~ 100 ° C        
Halbzeug
geglüht Zugfestigkeit (Rm) Härte [HBW] bei Temperatur
  <= 1.100 N/mm² <= 320 HBW ~ 20 ° C
vergütet 0,2% Dehngrenze (Rp0,2) /
bei Temperatur		 Zugfestigkeit (Rm) Bruchdehnung (A 5,65) Kerbschlagarbeit KV2
(ISO-V/Charpy-V)		 Probenlage
160 - 250 mm >= 800 N/mm² / ~ 20 ° C 900 - 1.100 N/mm² >= 12 % >= 50 Joule quer
160 - 250 mm >= 620 N/mm² / ~ 20 ° C 780 - 980 N/mm² >= 12 % >= 70 Joule quer
160 - 250 mm >= 520 N/mm² / ~ 20 ° C 700 - 850 N/mm² >= 10 % >= 70 Joule quer
<= 160 mm >= 800 N/mm² / ~ 20 ° C 900 - 1.100 N/mm² >= 15 % >= 40 Joule längs
<= 160 mm >= 620 N/mm² / ~ 20 ° C 780 - 980 N/mm² >= 15 % >= 50 Joule längs
<= 160 mm >= 520 N/mm² / ~ 20 ° C 700 - 850 N/mm² >= 12 % >= 50 Joule längs
  >= 515 N/mm² / ~ 350 ° C        
  >= 450 N/mm² / ~ 350 ° C        
  >= 620 N/mm² / ~ 300 ° C        
  >= 530 N/mm² / ~ 300 ° C        
  >= 460 N/mm² / ~ 300 ° C        
  >= 640 N/mm² / ~ 250 ° C        
  >= 545 N/mm² / ~ 250 ° C        
  >= 470 N/mm² / ~ 250 ° C        
  >= 665 N/mm² / ~ 200 ° C        
  >= 560 N/mm² / ~ 200 ° C        
  >= 480 N/mm² / ~ 200 ° C        
  >= 690 N/mm² / ~ 150 ° C        
  >= 575 N/mm² / ~ 150 ° C        
  >= 490 N/mm² / ~ 150 ° C        
  >= 720 N/mm² / ~ 100 ° C        
  >= 590 N/mm² / ~ 100 ° C        
  >= 500 N/mm² / ~ 100 ° C        
Walzdraaht
geglüht Zugfestigkeit (Rm) bei Temperatur
  <= 1.100 N/mm² ~ 20 ° C
vergütet Zugfestigkeit (Rm) bei Temperatur
160 - 250 mm 900 - 1.100 N/mm² ~ 20 ° C
160 - 250 mm 780 - 980 N/mm² ~ 20 ° C
160 - 250 mm 700 - 850 N/mm² ~ 20 ° C
<= 160 mm 900 - 1.100 N/mm² ~ 20 ° C
<= 160 mm 780 - 980 N/mm² ~ 20 ° C
<= 160 mm 700 - 850 N/mm² ~ 20 ° C
Gezogener Draht
geglüht Zugfestigkeit (Rm) Härte [HBW] bei Temperatur
  <= 1.100 N/mm² <= 320 HBW ~ 20 ° C
vergütet 0,2% Dehngrenze (Rp0,2) /
bei Temperatur		 Zugfestigkeit (Rm) Bruchdehnung (A 5,65) Kerbschlagarbeit KV2
(ISO-V/Charpy-V)		 Probenlage
160 - 250 mm >= 800 N/mm² / ~ 20 ° C 900 - 1.100 N/mm² >= 12 % >= 50 Joule quer
160 - 250 mm >= 620 N/mm² / ~ 20 ° C 780 - 980 N/mm² >= 12 % >= 70 Joule quer
160 - 250 mm >= 520 N/mm² / ~ 20 ° C 700 - 850 N/mm² >= 10 % >= 70 Joule quer
<= 160 mm >= 800 N/mm² / ~ 20 ° C 900 - 1.100 N/mm² >= 15 % >= 40 Joule längs
<= 160 mm >= 620 N/mm² / ~ 20 ° C 780 - 980 N/mm² >= 15 % >= 50 Joule längs
<= 160 mm >= 520 N/mm² / ~ 20 ° C 700 - 850 N/mm² >= 12 % >= 50 Joule längs
  >= 515 N/mm² / ~ 350 ° C        
  >= 450 N/mm² / ~ 350 ° C        
  >= 620 N/mm² / ~ 300 ° C        
  >= 530 N/mm² / ~ 300 ° C        
  >= 460 N/mm² / ~ 300 ° C        
  >= 640 N/mm² / ~ 250 ° C        
  >= 545 N/mm² / ~ 250 ° C        
  >= 470 N/mm² / ~ 250 ° C        
  >= 665 N/mm² / ~ 200 ° C        
  >= 560 N/mm² / ~ 200 ° C        
  >= 480 N/mm² / ~ 200 ° C        
  >= 690 N/mm² / ~ 150 ° C        
  >= 575 N/mm² / ~ 150 ° C        
  >= 490 N/mm² / ~ 150 ° C        
  >= 720 N/mm² / ~ 100 ° C        
  >= 590 N/mm² / ~ 100 ° C        
  >= 500 N/mm² / ~ 100 ° C        
Profile
geglüht Zugfestigkeit (Rm) Härte [HBW] bei Temperatur
  <= 1.100 N/mm² <= 320 HBW ~ 20 ° C
vergütet 0,2% Dehngrenze (Rp0,2) /
bei Temperatur		 Zugfestigkeit (Rm) Bruchdehnung (A 5,65) Kerbschlagarbeit KV2
(ISO-V/Charpy-V)		 Probenlage
160 - 250 mm >= 800 N/mm² / ~ 20 ° C 900 - 1.100 N/mm² >= 12 % >= 50 Joule quer
160 - 250 mm >= 620 N/mm² / ~ 20 ° C 780 - 980 N/mm² >= 12 % >= 70 Joule quer
160 - 250 mm >= 520 N/mm² / ~ 20 ° C 700 - 850 N/mm² >= 10 % >= 70 Joule quer
<= 160 mm >= 800 N/mm² / ~ 20 ° C 900 - 1.100 N/mm² >= 15 % >= 40 Joule längs
<= 160 mm >= 620 N/mm² / ~ 20 ° C 780 - 980 N/mm² >= 15 % >= 50 Joule längs
<= 160 mm >= 520 N/mm² / ~ 20 ° C 700 - 850 N/mm² >= 12 % >= 50 Joule längs
  >= 515 N/mm² / ~ 350 ° C        
  >= 450 N/mm² / ~ 350 ° C        
  >= 620 N/mm² / ~ 300 ° C        
  >= 530 N/mm² / ~ 300 ° C        
  >= 460 N/mm² / ~ 300 ° C        
  >= 640 N/mm² / ~ 250 ° C        
  >= 545 N/mm² / ~ 250 ° C        
  >= 470 N/mm² / ~ 250 ° C        
  >= 665 N/mm² / ~ 200 ° C        
  >= 560 N/mm² / ~ 200 ° C        
  >= 480 N/mm² / ~ 200 ° C        
  >= 690 N/mm² / ~ 150 ° C        
  >= 575 N/mm² / ~ 150 ° C        
  >= 490 N/mm² / ~ 150 ° C        
  >= 720 N/mm² / ~ 100 ° C        
  >= 590 N/mm² / ~ 100 ° C        
  >= 500 N/mm² / ~ 100 ° C        

 

 

 

 

 

Back to the overview and search.

Material request

Screenreader label 
SCR_________H________
2______D____S_C___EB8
XGH___E3O___I8S______
T_4____G______F___MUF
TBH___________N______
* mandatory field
Screenreader label

Company

Five reasons that are in favor of BASEDO STEEL

Learn more

Services

A short overview of our services

Learn more

Questions?

Would you like to ask us about your specific demands?

Contact us