Material 1.3980
Non-magnetizable steel
The material 1.3980 is an amagnetic steel with low thermal expansion.
1.3980 is usually supplied in the solution-annealed and aged condition.
Do you have any questions about the material or would you like to order? Complete our inquiry form, it`s free of charge and without obligation. We will get in touch with you in order to provide you with more information.
![1.3980 1.3980](/typo3temp/assets/images/1.3980_csm_werkstoffbild_b_535_a60d470c10_1d098a3597.jpg)
Standards
HDIN / EN | US-Standard | AFNOR | UNI | JIS | request |
---|---|---|---|---|---|
X5NiCrTiMoV26-15 | request |
Material Category: Non-magnetizable steel
Applications
Power engineering
Gas turbines
Cryogenics
Chemical Composition
C % | Si % | Mn % | P % | S % | Al % | B % | Cr % | Mo % | Ni % | Ti % | V % |
max 0,08 | max 1,00 | max 2,00 | max 0,030 | max 0,015 | max 0,3500 | 0,0030 - 0,0100 | 13,50 - 16,00 | 1,00 - 1,50 | 24,00 - 27,00 | 1,90 - 2,30 | 0,10 - 0,50 |
Product Specifications
SEW 390
Mechanical Properties
DIN SEW 390 (11/1991) Nichtmagnetisierbare Stähle. | ||||||
Stabstahl | ||||||
abgeschreckt | 0,2% Dehngrenze (Rp0,2) | Zugfestigkeit (Rm) | Bruchdehnung (A5, 65) | Kerbschlagarbeit (ISO-V/Charpy-V) | Probenlage | bei Temperatur |
<= 200 mm | >= 600 N/mm² | 900 - 1.200 N/mm² | >= 16 % | >= 55 Joule | längs | ~ 20 ° C |
<= 200 mm | >= 14 % | >= 30 Joule | quer | ~ 20 ° C |
Flacherzeugnisse | ||||||
abgeschreckt | 0,2% Dehngrenze (Rp0,2) | Zugfestigkeit (Rm) | Bruchdehnung (A5, 65) | Kerbschlagarbeit (ISO-V/Charpy-V) | Probenlage | bei Temperatur |
<= 20 mm | >= 600 N/mm² | 900 - 1.200 N/mm² | >= 16 % | >= 55 Joule | längs | ~ 20 ° C |
<= 20 mm | >= 14 % | >= 30 Joule | quer | ~ 20 ° C |
Rohr | ||||||
abgeschreckt | 0,2% Dehngrenze (Rp0,2) | Zugfestigkeit (Rm) | Bruchdehnung (A5, 65) | Kerbschlagarbeit (ISO-V/Charpy-V) | Probenlage | bei Temperatur |
<= 20 mm | >= 600 N/mm² | 900 - 1.200 N/mm² | >= 16 % | >= 55 Joule | längs | ~ 20 ° C |
<= 20 mm | >= 14 % | >= 30 Joule | quer | ~ 20 ° C |
Walzdraht | ||||||
abgeschreckt | 0,2% Dehngrenze (Rp0,2) | Zugfestigkeit (Rm) | Bruchdehnung (A5, 65) | Kerbschlagarbeit (ISO-V/Charpy-V) | Probenlage | bei Temperatur |
6 - 20 mm | >= 600 N/mm² | 900 - 1.200 N/mm² | >= 16 % | >= 55 Joule | längs | ~ 20 ° C |
6 - 20 mm | >= 14 % | >= 30 Joule | quer | ~ 20 ° C |
Schmiedestücke | ||||||
abgeschreckt | 0,2% Dehngrenze (Rp0,2) | Zugfestigkeit (Rm) | Bruchdehnung (A5, 65) | Kerbschlagarbeit (ISO-V/Charpy-V) | Probenlage | bei Temperatur |
<= 200 mm | >= 600 N/mm² | 900 - 1.200 N/mm² | >= 16 % | >= 55 Joule | längs | ~ 20 ° C |
<= 200 mm | >= 14 % | >= 30 Joule | quer | ~ 20 ° C |